PPA-CF vs PA6-CF?
Does anyone have experience printing PPA-CF and PA6-CF? I had read that "PPA-CF is 48% stronger" than PA6 if you get good layer adhesion, but I'm seeing conflicting info regarding impact resistance. Anyone have input who's printed and used both?
What about PAHT-CF? Seems underrated. Tensile properties look good.
I am assuming you are talking about bambu lab PAHT which as mentioned is just a marketing team (although, PPA is not a specific chemical name either iirc)
Bambu lab PAHT is WAY overpriced for what you are getting, especially relative to sirayatechs offerings.
QIDI seems to be better in terms of pricing.
qidi/fusrock/phaetus are all the same so if you want their PET/PPA just buy whatever is cheaper. I still haven't found anything that beats the price/perf of sirayatech though.
Discuss anything GunCAD related. If you need help, see /c/help. If you think you're discussing a thing a lot of the time, consider making your own separate community.
Abide by the global rules or be smitten.
Shitty stock image may be changed at moderator discretion.